Repar Monosteel

The anti-corrosive effectiveness of Repar Monosteel results from the high alkalinity and from the superpozzolanic reactivity of components. The specific corrosion inhibitor contained in the compound (DCI - Corrosion Inhibitor Agrèment Certificate BBA** n.96/3232), conforming to the standard UNI 9747, is based on a reaction which is capable of making unavailable the ferrous ions for the supply of the electrochemical processes of corrosion. The polymeric components of Repar Monosteel also determine further increases in the effectiveness against corrosion, especially vis-à-vis the aggressive attacks arising from chlorides and sulphates. (BBA = British Board of Agrèment).

Carefully remove loose rust from the metal surfaces of exposed reinforcing bars by sandblasting or deep brushing until the white metal surface is obtained. This operation is essential to effectively develop the anticorrosive property of Repar Monosteel. Obviously, to block the advance of the carbonation profile in the concrete, it is essential to complete the restoration with the appropriate restoration mortars: thixotropic (Repar line) or pourable (Grout line).

Place about half a litre of water in a bucket, gradually add Repar Monosteel and the additional water needed to achieve a fluid, dense, brushable consistency (about 8 - 10 litres of water for a 25 kg bag). Continue mixing until a smooth, lump-free mixture is obtained. Apply with a brush to the surfaces of the previously prepared reinforcing bars. To prevent the application of the repair mortar from removing the still fresh Repar Monosteel treatment, wait for the product to harden before proceeding with the volumetric restoration. The minimum recommended waiting time is about 6-8 hours with summer temperatures and about 12-16 hours with winter temperatures. Do not apply the product with temperatures below 5°C or if it is expected that the temperature may fall below this value during the first 12 hours of curing.